Magnesium Alloy Extruded Tooling Plate|sheet AZ31B /ZK60A Can Be Super Formed at Elevated Temperatures

Product Detail

Magnesiul Alloy Extruded Tooling Plate|sheet AZ31B /ZK60A Can Be Super Formed At Elevated Temperatures

Magnesium alloy plate

Or called magnesium alloy extruded plate

Main application:

It is in wide variety of uses including aircraft fuselages, cell phone and laptop cases, speaker cones and concrete tools. Especially AZ31B plate can be super formed at elevated temperatures to produce a wide variety of intricate components for automotive uses. It is also available as tooling plate which is specially produced to provide a flat plate surface. Usually buyer after get it ,will make some CNC machining process ,make it into all kinds of complex parts.

Magnesium alloy extruded plate producing method:

Magnesium alloy billet (cast) ? extruded process ?leveling process ?cutting process ?packing



Normal material used:

AZ31B, AZ61A, AZ80A, ZK60A

Chemical composition:



 

 

Main Mechanical properties:

Depends on the material and final shape, take AZ31B plate as sample ,

Tension strength at about 275 mpa

Yiled strength at about 180mpa

Elongation at about 12%

Some reference of mg alloy plate as below:

 




	Strength Property
Shop   Sign	Thickness(mm)	Tensile   Strength Rm (N/mm2)	Yield   Strength Rp0.2 (N/mm2)	Elongation (A%) 50mm
AZ31B	0.5-3.0	260	170	24
	3.0-10.0	230	140	18
M2M	0.8-3.0	190	110	6
	3.0-5.0	180	100	5
	5.0-10.0	170	90	5
AZ40M	0.5-3.0	280	180	17
	3.0-5.0	260	160	14
AZ41M	0.8-3.0	290	190	17
	3.0-5.0	270	170	14
ME20M	0.8-3.0	250	170	21
	3.0-10.0	220	140	15